直销美国杜邦超耐磨脱模级POM Delrin 100ALE
Density
|
1.40
|
g/cm3
| ISO 1183 |
|
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)
|
2.5
|
g/10 min
| ISO 1133 |
|
Molding Shrinkage
|
|
| ISO 294-4 |
|
Across Flow
|
1.7
|
%
|
|
|
Flow
|
2.0
|
%
|
|
| Mechanical | Nominal Value
|
Unit
|
Test Method
|
|
Tensile Modulus
|
3000
|
MPa
| ISO 527-2 |
|
Tensile Stress (Yield)
|
70.0
|
MPa
| ISO 527-2 |
|
Tensile Strain (Yield)
|
18
|
%
| ISO 527-2 |
|
Nominal Tensile Strain at Break
|
40
|
%
| ISO 527-2 |
|
Poisson&＃39;s Ratio
|
0.37
|
|
|
| Impact |
Nominal Value
|
Unit
|
Test Method
|
|
Charpy Notched Impact Strength
|
|
| ISO 179/1eA |
|
-30°C
|
8.0
|
kJ/m2
|
|
|
23°C
|
11
|
kJ/m2
|
|
|
Charpy Unnotched Impact Strength
|
|
| ISO 179/1eU |
|
-30°C
|
200
|
kJ/m2
|
|
|
23°C
|
No Break
|
|
|
|
Notched Izod Impact Strength (23°C)
|
8.0
|
kJ/m2
| ISO 180/1A |
| Thermal | Nominal Value
|
Unit
|
Test Method
|
|
Melting Temperature 2
|
178
|
°C
| ISO 11357-3 |
|
Annealing Temperature
|
160
|
°C
|
|
|
Annealing Time - Optional
|
30.0
|
min/mm
|
|
POM具有很低的摩擦系数和很好的几何稳定性，特别适合于制作齿轮和轴承。
POM具有耐高温特性，因此还用于管道器件（管道阀门、泵壳体），草坪设备等。
POM是一种坚韧有弹性的材料，即使在低温下仍有很好的抗蠕变特性、几何稳定性和抗冲击特性。
POM的高结晶程度导致它有相当高的收缩率，可高达到2%~3.5%。对于各种不同的增强型材料有不同的收缩率。
POM属结晶性塑料，熔点明显，一旦达到熔点，熔体粘度迅速下降。